RING AND SNOW BALL FORMATION
IN THE KILN
Sinter Ring at the junction of burning zone and transition zone
Spurrite andSulfo-spurrite ring
In calcining zone
8/18/2019 formation des anneaux four rotatif
2/39
Reduction in kiln
Diameter due toRing formation
8/18/2019 formation des anneaux four rotatif
3/39
Raw mix ChemistryVariation in chemistry
Flame &temperature
Un stable kiln and
calciner operation
Key reasons for ring formation
Combustion
Selection of
refractories
Hard Burning
Due to the presence ofCalcite and Quartzite Volatile
recycling
All reasons are inter-dependent and flameand combustion plays a very major role
Fuel characteristics
8/18/2019 formation des anneaux four rotatif
4/39
The formation of a ring is a dynamic process in which thefactors responsible for formation outweigh the forces of
destruction.The forces considered to cause deposit formation can begrouped as follows:
• Melting or freezing due to addition or removal of heat.
• Interlocking of aggregates built up of finer particles hold
together by surface forces.
• Interlocking of long fibrous particles.
8/18/2019 formation des anneaux four rotatif
5/39
In general, chemical composition of the sinter ring material is that ofthe clinker with no appreciable concentration of volatile elements.
From a mineralogical viewpoint, the normal clinker minerals like alite,belite and free CaO are observed. The bonding mechanism
responsible for sinter ring formation is the freezing of the clinker.The rings, depending on their origin, may be dense or porous, and
may develop slowly or just in a few hours. The first symptoms ofring formation are:
SINTER RING
• A higher negative pressure before the exhaust fan.• Incomplete fuel combustion as indicated by "CO" analyzer.
• Intermittent charge retention.• Abnormal temperature gradients in the kiln shell.
• Higher amperages in the kiln motor.The reasons for ring formation, well agreed between many plant
operators, may be classified in three groups:
• Process.
• Operation.• Maintenance.
8/18/2019 formation des anneaux four rotatif
6/39
The next group deals with operation troubles that can lead to
ring formation. These are:
• Discontinuous feed.
• Material segregation.
• Flame pattern and position.
• Improper combustion.
• Successive kiln upsets.
8/18/2019 formation des anneaux four rotatif
7/39
Material segregation is not an uncommon situation inrotary kiln. For instance, the lime content we have in the
meal, loss on ignition free, never coincides with the limecontent in the clinker. The lighter lime particles are easilycarried by the gases, while silica, iron oxide and alumina
.Depending on the degree of segregation, excess liquid mayform in the burning zone, and even outside, if the meltingpoint of the glass is lowered by segregation. The addition of
sand in the raw materials modifies significantly the burnabilitybecause it shows lower reactivity and grindability. Thegrinding of quartz, during assemblage grinding, causes quartzconcentration in the coarse fractions of raw mix and
consequently material segregation in the kiln charge.
8/18/2019 formation des anneaux four rotatif
8/39
In the maintenance group we find:
• Defective burner.
• e ec ve ns rumen a on.
• False air admission
8/18/2019 formation des anneaux four rotatif
9/39
8/18/2019 formation des anneaux four rotatif
10/39
Calcium LangebeiniteK2Ca2(SO4)3
>1250 ______
8/18/2019 formation des anneaux four rotatif
11/39
8/18/2019 formation des anneaux four rotatif
12/39
Porosity of the brick may help to reduce ring formation but at
the cost of heat loss. It can be reduced but it cannot be avoided.
Closed pores
Porosity of the kiln brick
Open pores
Silica infiltrated surface or vitrified surface on brick can avoid infiltration of low melting ,loViscous components .This avoids destruction of refracories but spurrite rings cannotbe avoided fully. Properly balanced chemistry , well tuned flame with hot and oxdised
conditions and properly operated kiln and Calciner can only elimiinate ring formation orreduce the aggravation.
8/18/2019 formation des anneaux four rotatif
13/39
Uniform coatingPreferably 5 or 6 %Of the diameterStrong intense flame plays a major role
In kiln coatng stablity
8/18/2019 formation des anneaux four rotatif
14/39
What is the different between sulphur, spurrite, and alkali ringsand how can we distinguish between these three?
Formation of type of ring is based upon the kiln system
atmosphere.If sulfur is excess in raw material and fuel thensulphate ring is formed due to formation of spurrite andsulphospurrite mineral.Sulphate ring generally formed incalcination zone and it is very hard in nature.Alkali ring is
formed when alkali is present in excess than the sulphur inraw material and fuel.When high alkali concentration in rawmaterial then Arcanite(K2SO4),Aphthitalite[K3Na(SO4)2] , andThenardite[Na2SO4] mineral formed.You may analyse the
coating sample by XRD to know the cause of coatingformation and type of ring.
8/18/2019 formation des anneaux four rotatif
15/39
Sulphur Rings: Sulphur-induced rings are formed when the
molar sulfur to alkali ratio inthe system is more than 1.2. In such cases, there is aconsiderable amount of free SO3 circulating in the kiln. At a
certain concentration level in the kiln gas, sulfation of the freelime occurs with anhydrite formation (CaSO4). If the kiln isburning under slightly reducing conditions, more volatile andlower melting sulfur salts may form, therefore increasing the
severity of the problem. The salts, in molten state, coat thetraveling clinker dust, forcing it to stick to the kiln wall in the formof rings. Sometimes the chemical analysis of such rings doesnot indicate high sulfur concentrations, proving that even a small
amount of free sulfur is sufficient to cause rings. The severity ofthe problem increases with the dust concentration in the kilngas. Dustier kilns have a tendency to form more rings thancleaner kilns.
8/18/2019 formation des anneaux four rotatif
16/39
Spurrite Rings:Carbonate or spurrite rings are formed throughCO2desorption intothe freshly formed free lime, or even through beliterecarbonation. These rings are hard, layered, and exhibit the
same chemistry as regular clinker. X-ray diffraction however,clearly indicates the presence of spurrite, a mineral withcomposition C2S.CaCO3.S urrite is a form of carbonated belite. When the carbonate in
the spurrite is replaced with sulfur the new mineral is calledsulfated spurrite. Spurrite rings form whenever the partialpressure of CO2 above the bed of material is high enough toinvert the calcining
reaction. In coarsely ground, silica-rich raw mixes, the free limedoes not have sufficient time in the calcining zone to react withsilica, therefore increasing the chances for spurrite deposits.
8/18/2019 formation des anneaux four rotatif
17/39
Alkali rings:The third type of ring occurs whenever the sulfur-to-alkali
molal ratio is( encrustration index)less than 0.83, usually in kilns with heavy chlorine loads. In suchcases, low-melting potassium salts provide the binder for clinker
dust travelling up the kiln. Through a "freeze-and-thaw"
mechanism, these rings can assume massive proportions. Alkalirings are far less common than other types because sulfur andcarbonates usually are in excess relative to potassium. In lime
, ,
sulfur, severe ringing and balling sometimes occur.
8/18/2019 formation des anneaux four rotatif
18/39
-Statement by an experienced process man
8/18/2019 formation des anneaux four rotatif
19/39
Long and lazy flame reduce the calcining zone length and increase the temperature. It increases
Volatility of sulfur and alkalies ,increase the recirculation, and increase the low melting sufites .Therawmeal soaked in this temperature, in this low melting alkali and calcium sufites. gets balled up .Asit reaches the burning zone it steals some more liquid , increases its size and many times blocks theflame causing deflection and impinges causing damage the refractory..
Snow ball formation
8/18/2019 formation des anneaux four rotatif
20/39
around
1200 deg c
8/18/2019 formation des anneaux four rotatif
21/39
Spurrite ring in kiln calcining zone
8/18/2019 formation des anneaux four rotatif
22/39
Sulfo Spurrite -SEM
8/18/2019 formation des anneaux four rotatif
23/39
8/18/2019 formation des anneaux four rotatif
24/39
Chemical Analysis of spurrite ring layer by layer-- study by RHI,Vienna
8/18/2019 formation des anneaux four rotatif
25/39
Sulfo Spurrite ring -SEM
8/18/2019 formation des anneaux four rotatif
26/39
This is the result of bad flame which I witnessed In my own plant in my shorttenure. 72 hours stoppage , loss of 11000 tons of clinker or 11 million Indian
rupees as net cash loss. More over it is an unsafe activity
8/18/2019 formation des anneaux four rotatif
27/39
Do you need such condition and stoppage of kiln ?.Snow ball formation as a result of ring formation and bad flame.Low gas retention time in calciner further aggravate the situationwhich we directly witnessed it. ILC is less friendly than SLC as faras gas retention and combustion efficiency is concerned but NOXemission is higher in SLC than that of in ILC wheredenoxification is achieved.
8/18/2019 formation des anneaux four rotatif
28/39
Bad flame activate the volatile
recirculation esp sulfur and alkalies
8/18/2019 formation des anneaux four rotatif
29/39
Short and intense flame ,low back end temperature ,low volatile recycle
More absorption of sulfur and formation of more
thermally stable sulfates of alkali and calcium
Favorable temperatureprofile
Influence of flame length on volatile recycle and thermal stability
1500degc
1200
Long flame ,high back end temperature ,high volatile recycle
Less sulfur volatile absorption and formation of more
thermally unstable stable sulfites of alkali and calcium
Unfavorable Temperatureprofile, flat
Favorable area for spurrite ring
formation
1000
1500
1200
1000
8/18/2019 formation des anneaux four rotatif
30/39
(- Reference from PCA)
8/18/2019 formation des anneaux four rotatif
31/39
Reference from Blue circle literature
( Holcim)
8/18/2019 formation des anneaux four rotatif
32/39
Fives Pillard’s novaflam got the ability to slice the ring and
avoid 3 days Stoppage.
The burner can be more inclined ,shape the flame closer to the ring which reduces theThickness. The jack and knuckle ball arrangement in the telescopic piece allow thisup and down motion Which only Nova flam has.
8/18/2019 formation des anneaux four rotatif
33/39
Pillard ‘s Novaflam got the ability to slice the ring and avoid 3 days
Stoppages.
The burner can be more inclined ,shaped the flame closer to the ring which reduces theThickness. The jack and knuckle ball arrangement in the telescopic piece allow thisup and down motion Which only Nova flam has..Caution –extra care must be takenWhen High alumina bricks are used which is inferior in its thermal properties thanmagnesite Bricks.
8/18/2019 formation des anneaux four rotatif
34/39
Shark teeth forms when ash in coal is high and high dust circulation from cooler to kiln.This makes the clinker more sticky and many occasions lead to snow man formation onStatic cooler and rhino horn on burner. Chemistry ,if it is not controlled can lead to dustyClinker and shark teeth at the kiln tip.By pushing the burner in and adjusting flame givesgreat relief to this problem.Cooler air distribution also reduces this problem.
Shark teeth lead segregation in the clinker discharge and leads to red river in the cooler .
ar ee
8/18/2019 formation des anneaux four rotatif
35/39
By simple to and fro movement of swirler tip and by alteration of primary airPressure at burner inlet , can change length and shape of the flame.Novaflam is user friendly ,simple and very versatile burner.
8/18/2019 formation des anneaux four rotatif
36/39
8/18/2019 formation des anneaux four rotatif
37/39
DdD
Do you need a old time master burner who does jugglery now and then to tune the flameby adjusting two or three valves for axial,radial and stabilising air like a
magician on the Stage. Nova flam says “NO”. Novaflam has simple operation unlikecomplicated operation with other burners. More user friendly than any other burner.
8/18/2019 formation des anneaux four rotatif
38/39
Make the kiln smile with good flameor you will weep
Novaflam makes you to smile
8/18/2019 formation des anneaux four rotatif
39/39
Thank you for your kind attention
Technical advisor - commissioning
Fives combustion pvt ltdBaroda