Acronal® PRO 80
a next generation polymer emulsion for medium-duty
anti-corrosion primers, fillers or topcoats for industrialmetal coatings
page 1 of 2® registered trademark of
BASF Group
Key features and
benefits
• enhanced corrosion
protection
• exellent barrier andinhibiting properties
• APEO- and zinc-free
• good adhesion
• good early rain
resistance
• high PVC
• low odor
C APRO80e/12-2008
General information
Typical physical characteristics (not to be considered specifications)
appearance white emulsionsolids by weight ~ 50 %
viscosity at 23 °C (73 °F) (DIN EN ISO 3219) ~190 mPa.s
pH ~ 8.5
specific mass as supplied 1,090 kg/m³
minimum film-forming temperature ~ 22 °C (72 °F)
freeze/thaw stable no
preliminary datasheet
PROtective (high performance anti-corrosion) or
PROfessional (Industrial environment friendly)
7/22/2019 Acronal Pro 80
http://slidepdf.com/reader/full/acronal-pro-80 2/4
Applications
Acronal® PRO 80 is a unique barrier and inhibiting polymer emulsion for medium-duty anti-corrosion primers, fillers or
topcoats (ISO 12944-2:C2-C3 or C3-C4).
Performance
Acronal® PRO 80 offers exceptionally high salt-spray resistance (ca. > 700 hours) with dry film thickness of 80
microns.
This new barrier and inhibiting product offers an active corrosion protection barrier against oxygen water and other
ions that cause surface erosion as well as good early rain resistance and excellent adhesion.
C APRO80e/12-2008 page 2 of 4 Acronal® PRO 80
7/22/2019 Acronal Pro 80
http://slidepdf.com/reader/full/acronal-pro-80 3/4
Formulation Guidelines
Acronal® PRO 80 is compatible with a variety of anti-corrosion additives. The product provides the possibility to
formulate with a range of reactive anti-corrosion pigments, especially those based on zinc phosphates.
The minimum film-forming temperature of Acronal® PRO 80 is approximately 22 °C. Suitable film-forming agents
should generally be added to achieve homogeneous films at lower temperatures. The recommended addition is 2-4
% of a blend of white spirit and 2-butoxyl ethanol and/or 2-(2-butoxyethoxy) ethanol or
phenoxy propanol).
Viscosity and flow can be adjusted by adding thickeners, preferably in the final stage of production. In
particular from the corrosion-protection aspect, associative thickeners such as Collacral® PU 85 are time-
tested. Good leveling and Newtonian flow can be achieved with water-miscible solvents present. In aqueous anti-
corrosion formulations, the proportion of thickener should not exceed 1 %, calculated as solids on solid binder.
C APRO80e/12-2008 page 3 of 4 Acronal® PRO 80
7/22/2019 Acronal Pro 80
http://slidepdf.com/reader/full/acronal-pro-80 4/4
BASF Nederland B.V.
Performance Chemicals
P. O. Box 390
8440 AJ Heerenveen, The Netherlands
Phone +31 513 619 619
Fax +31 513 619 600
www.basf.com/resins
C APRO80e/12-2008 page 4 of 4 Acronal® PRO 80
Safety
When handling these products, advice and information given in the safety data sheet must be complied with. Further, protective and
workplace hygiene measures adequate for handling chemicals must be observed.
Note
The data contained in this publication are based on our current knowledge and experience. In view of the many factors that may affect
processing and application of our product, these data do not relieve processors from carrying out their own investigations and tests;
neither do these data imply any guarantee of certain properties, nor the suitability of the product for a specific purpose. Any descriptions,
drawings, photographs, data, proportions, weights, etc. given herein may change without prior information and do not constitute the
agreed contractual quality of the product. It is the responsibility of the recipient of our products to ensure that any proprietary rights and
existing laws and legislation are observed.