Cold Spray Powder

Metal PowderProduct Name Particle Size Chemical

Composition (%)Bulk Density　　 (g / cm3)

Particle Morphology Remarks

PG-PMP-1010 -45µm CuFeSnPbMn

><<<<

99.30.010.010.010.01

3.552 ・Water atomized

Copper Powder

PG-PMP-1013 -10µm CuFeSnPbMn

><<<<

99.60.010.010.010.01

3.884 ・Water atomized

PG-PMP-1014 -90µm CuFeSnPbNi

><<<<

99.90.0060.0010.0010.0042

5.28 ・Gas atomized

Aluminum PowderPG-PMP-1020 -45µm Al

SiFeCuMn

><<<<

99.70.150.20.020.02

1.36 ・Gas atomized

Cold Spray Powder

PG-PMP-1016 -53µm CuFeSnPbNi

><<<<

99.90.0060.0010.0010.0042

・Gas atomized

PG-PMP-1012 -20µm CuFeSnPbMn

><<<<

99.60.010.010.010.01

・Water atomized

PG-PMP-1017 30~45µm CuFeSnPbMn

><<<<

99.50.010.010.010.01

Although the particle shapes are irregular, the shape does not harm the powder flowability and the powder has high electric conductivity.

Metal PowderProduct Name Particle Size Chemical

Composition (%)Bulk Density　　 (g / cm3)

Particle Morphology Remarks

PG-PMP-1060 -45µm ZnPbFeCd

><<<

99.50.00180.00050.0002

2.668 ・Water atomized

Zinc Powder

Tin PowderPG-PMP-1070 150 ~ 63µm Sn

FePbCuS

><<<<

99.50.080.020.020.02

3.84 ・Water atomized

Niobium PowderPG-PMP-1080 30~10µm Nb

TaMgFeMo

><<<<

99.80.00150.000030.000010.00001

・Crushing

Tantalum PowderPG-PMP-1090 30~10µm Ta

WMoNbP

><<<<

99.90.0000030.0000010.0000010.000001

・Crushing

Cold Spray Powder

PG-PMP-1050 63~5µm AgCuSnPbBi

><<<<

99.50.20.010.010.01

5.012 ・Water atomized

Silver Powder

Nickel PowderPG-PMP-1032 35~15µm Ni

FeCoSiC

<<<<<

1000.10.10.050.05

4.364 ・Water atomized

Titanium PowderPG-PMP-1040 -45µm Ti

OFeNC

><<<<

99.70.170.080.030.03

2.536 ・Gas atomized

Metal PowderProduct Name Particle Size Chemical

Composition (%)Bulk Density　　 (g / cm3)

Particle Morphology Remarks

Low Carbon Steel PowderPG-PMP-1100 -45µm Fe

OSCTi

><<<<

990.090.00680.0030.01

・Water atomized

Cold Spray Powder

A Revolution in Spray Coating TechnologyNearly 100% Deposition EfficiencyPLASMA GIKEN’s Innovative Heat-Gun Integrated Cold Spray Unit

Alloy PowderProduct Name Particle Size Chemical

Composition (%)Bulk Density　　 (g / cm3)

Particle Morphology Remarks

PG-AMP-1010 45~10µm FeCrNiMoSi

<<<<

Balance18.014.03.01.0

2.78 ・Water atomized

SS316L Powder

SS304 PowderPG-AMP-1020 -45µm Fe

CrNiMnSi

<<<<

Balance20.011.00.80.6

2.764 ・Water atomized

SS430 PowderPG-AMP-1040 -45µm Fe

CrMnSiC

<<<<

Balance18.01.00.750.12

2.86 ・Water atomized

Ni625 PowderPG-AMP-1060 25~5µm Ni

CrMoFeTa

<<<<

Balance22.02.02.01.0

3.212 ・Gas atomized

Ni718 PowderPG-AMP-1070 32~10µm Ni

CrFeNbTa

<<<<

Balance21.018.55.01.0

3.356 ・Gas atomized

Ni738 PowderPG-AMP-1080 25~5µm Ni

CrCoTiAl

<<<<

Balance16.08.53.53.5

3.628 ・Gas atomized

CoNiCrAlY PowderPG-AMP-1100 37~5µm Co

NiCrAlY

<<<<

Balance32.021.08.00.5

3.924 ・Gas atomized

Cold Spray Powder

Cold Spray Powder

Alloy PowderProduct Name Particle Size Chemical

Composition (%)Bulk Density　　 (g / cm3)

Particle Morphology Remarks

NiCoCrAlY Powder

Ti-6Al-4V Powder

PG-AMP-1110 45~10µm NiCoCrAlY

<<<<

Balance22.015.011.50.2

3.668 ・Gas atomized

Zn-2Al Powder

PG-AMP-1120 -45µm TiAlVFeC

<<<<

Balance6.04.00.40.2

1.508 ・Gas atomized

80Ni-20Cr Powder

PG-AMP-1130 -53µm ZnAlFeCuSn

<<<<

Balance2.00.00040.00020.0001

3.424 ・Gas atomized

White Metal Powder

PG-AMP-1140 53~20µm NiCrSiFeB

<<<<

Balance20.01.751.00.5

4.216 ・Gas atomized

Zn-50Sn Powder

PG-AMP-1150 -63µm SnSbCuZnAg

<<<<

Balance15.020.01.00.1

・Gas atomized

PG-AMP-1160 -53µm ZnSnPbFe

<<<

Balance50.00.020.02

1.484 ・Gas atomized

A6061 PowderPG-AMP-1170 -90µm Al

MgSiFeCu

<<<<

Balance1.20.80.70.15

・Gas atomized

Rotatable Sputtering Targets Electric Conductive Parts

Product Examples

As SpraySpray Powder : Ni718

Machining after Spray

Machining before Spray

Repair of Labyrinth Seal

PLASMA GIKEN CO., LTD.

■ Headquaters & Sales Office / Saitama Application and R&D Center

4-1 Imaichi, Yorii - machi, Osato - gun Saitama, 369-1214, JapanTEL : +81 (0)48 577 1225 FAX : +81 (0)48 582 0095URL : http://www.plasma.co.jp

The New Generation of Cold Spray Technology

2016.03.01