Product Data SheetProduct Data Sheet

CANUSA

-CPS

Wraparound Sleeve for Offshore Heated Infill Systems

CANUSA-CPS is registered to ISO 9001:2008.

2-Layer

Wrapid Sleeve

Standard Shrink

Girth-Weld Joints

Oil & Gas

Infill Systems

Reel, J & S Lay

MIS-65 / MIS-100

Unique Adhesive Technology

MIS-65 and MIS-100

MIS-65

and MIS-100

MIS-65 and MIS-100

Maximize Cost Savings

Canusa's unique (open time) adhesive

technology allows for lower installation

preheat temperatures, superior adhesion to

a wide range of mainline pipe coatings and

consistent performance in rugged offshore

environments. The adhesive has been

formulated to provide long-term adhesion

and excellent cathodic disbondment

resistance properties.

Hot Mast ic & Foam Inf i l lCompatibility

sleeves can be used

with hot mastic pour, polyurethane foam or

other infill systems to provide effective

long-term corrosion protection.

sleeves are resistant to hot

mastic pour systems and meet the

requirements of the Drum Skin Test for

high temperature effects.

Precious time is saved in several areas when

using sleeves on

laybarge operations in combination with

infill systems; lower preheat temperature

equates to lower installation times, single

wrap configuration eliminates the

requirements for muitiple wrapping, and

the pre-attached closure seal means less

time is used handling, positioning and

installing the joint protection materials.

The overall system minimizes installation

time and labour costs while promoting high

production rates.

Applications

Temperature Range

Pipe Sizes

55 - 1220 (2 - 48)

up to 100C (212F)

Configurations

For more than 35 years, Canusa-CPS has

been a leading developer and manufacturer

of specialty pipeline coatings for the sealing

and corrosion protection of pipeline joints

and other substrates. Canusa-CPS high

performance products are manufactured to

the highest quality standards and are

available in a number of configurations to

accommodate many specific project

applications.

sleeves have a

patented one-piece construction that

incorporates a pre-attached closure seal.

This contributes to a rapid and consistent

field installation procedure. Without any

requirements for the wrapping of multiple

layers, the field installation is fast, efficient

and in-line with timing requirements of

offshore laybarge operations. The

crosslinked high-density polyethylene

(HDPE) backing is designed to provide a

rapid and consistent shrink response when

installed with propane torch equipment.

sleeves can be

conveniently wrapped and installed in low

ambient temperatures due to its excellent

low temperature flexibility attributes.

Corrosion Protection of Girth-Welds under heated infill systemson offshore service environments

Flexible & Time EfficientInstallation

Product Description

Features & Benefits

MIS-65 and MIS-100 heat-shrinkable

sleeves provide superior corrosion

protection and effective long-term

adhesion to pipelines operating offshore at

temperatures up to 100C (212F). MIS-65

and MIS-100 sleeves are specifically

engineered for use in combination with hot

marine mastic pour, polyurethane foam or

other infill systems. MIS-65 and MIS-100

sleeves are resistant to the severe

conditions of hot mastic pour operations

and maintain their full set of anti-corrosion

properties. MIS-65 and MIS-100 are fully

compatible with a wide range of pipeline

coatings, including PP, FBE, PE, Coal Tar and

Tape.

MIS-65 and MIS-100

MIS-65 and MIS-100

Offshore Pipelines

Wraparound Sleeve for Offshore Heated Infill SystemsMIS-65 / MIS-100

Canusa warrants that the product conforms to its chemical and physical description and is appropriate for the use stated on the installation guide when used in compliance with Canusas written instructions. Since many installation factors arebeyond our control, the user shall determine the suitability of the products for the intended use and assume all risks and liabilities in connection therewith. Canusas liability is stated in the standard terms and conditions of sale. Canusa makes noother warranty either expressed or implied. All information contained in this installation guide is to be used as a guide and is subject to change without notice. This installation guide supersedes all previous installation guides on this product.E&OE

Printed on recycled paper. Recyclable.

www.canusacps.com

PDS-A4-MIS-65&100-rev014

The product selection chart shown here is intended as a guide for standard products.Consult your Canusa representative for specific projects or unique applications.

Back

ing

Sle

eve

Resi

stance

toIn

fill

Typical Product Properties

102 (216)40 (58)

24 (3480)700500pass52301020

> 8 Jno holiday @ 10kV

80 (46)65 (37)

< 7pass0.05

-14 (7)no melt or sag

1.8 (73)

pass, no holidays @ 10kV< 10%< 15%< 15%

18

< 7

124 (255)52 (75)

24 (3480)700500pass52301020

> 8 Jno holiday @ 10kV

115 (66)90 (51)

pass0.05

-15 (5)no melt or sag

1.8 (73)

pass, no holidays @ 10kV< 10%< 15%< 15%

18

< 7< 7

UnitTest Standard MIS-100MIS-65

C (F)N/cm (psi)

MPa (psi)%%

VisualShore D

mgohm-cmkV/mm

----

N/cm (pli)N/cm (pli)mm radmm radVisual

%C (F)Visual

mm (mils)

Visual%%%

2

ASTM E28DIN 30 672

ASTM D638ASTM D638ASTM D638ASTM D2671ASTM D2240ASTM D1044ASTM D257ASTM D149

DIN 30 672DIN 30 672ASTM D1000DIN 30672ASTM G8ASTM G42, 48hrsASTM D870ASTM D570ASTM D2671-CD024 A P50-F SD004

pipe 24, mold 26, mastic @ 200CASTM D1000ASTM D638ASTM D638

Softening pointLap shear @ 23C

Tensile strengthElongationHeat Aging - Elongation @ BreakHeat Shock - 4hrs @ 250CHardnessAbrasion resistanceVolume ResistivityDielectric Strength

ImpactIndentation ResistancePeel Strength to Steel, PE, PPPeel Strength @ 23CCathodic Disbondment @ 23CCathodic Disbondment @ 65CHot Water ImmersionWater AbsorptionLow Temp. FlexibilityDrum Skin Test

Visual InspectionChange in Peel StrengthChange in Tensile StrengthChange in Elongation

Fully Recovered Thickness

How To Order:

300, 450, 600, 700mm (12, 18, 24, 28")

Pipe Size

Colour BK- Black

55 - 1220mm (2 -48")

Heated Infill Systems

MIS-65 - MIS-100 -65C (149F) 100C (212F)

0.88mm (35 mils)

Sleeve Width

Backing (thickness as supplied)

Backing (thickness fully recovered)

Adhesive (thickness as supplied)

Maximum Operating Temperature

MIS-65 315-450 BK

Dim

ensi

ons

&O

rderi

ng

Info

Standard MIS-65 and MIS-100 Optionssleeve

width

The above represent standard ordering options. Consult your Canusa representative for any unique project requirements or CanusaWrap configuration.

Min. Sleeve Width =50 mmBare Steel Dimension + (2")

on each side of the pipe joint.

0.63mm (25mils)

0.80mm (32mils)

Celsius

105

90

75

60

45

30

Fahrenheit

221

194

167

140

113

86

Sle

eve

Opera

ting

Chara

cteri

stic

sProduct Selection Guide

MIS-100MIS-65

90C (194F)

100C (212F)

excellent

excellent

excellent

Tape, FBE, PE, PP

St 3 (min) SA 2(rec)

65C (150F)

65C (149F)

excellent

excellent

excellent

Bit, Tape, CTE, FBE, PE

St 3 (min) SA 2(rec)

Minimum Installation Temperature

Maximum Operating Temperature

Resistance to Hot Infill Pour

Compatibility to Hot Marine Mastic

Compatibility to Polyurethane Foam

Main Line Coating Compatibility

Recommended Surface Preparation

PipelineOperatingTemperature

Pre-heatTemperature

Choose your sleeve based on

Operating Temperature and

Characteristics listed below.

pipesize

Adhesi

ve

Application

CANUSA-CPSSHAWCOR LTDa division of .

25 Bethridge RoadToronto, OntarioM9W 1M7,CanadaTel: +1 (416) 743-7111Fax: +1 (416) 743-5927

Canada U.S.A./Latin AmericaCANUSA-CPS

SHAWCOR INC.a division of2408 Timberloch PlaceBuilding C-8The Woodlands, Texas77380, U.S.A.Tel: +1 (281) 367-8866Fax: +1 (281) 367-4304

Europe/Middle East Asia/PacificCANUSA-CPSa division of Canusa Systems Ltd.Unit 3, Sterling ParkGatwick RoadCrawley, West SussexEngland RH10 9QTTel: +44 (1293) 541254Fax: +44 (1293) 541777

CANUSA-CPSa division of .#05-31, Blk 52, FrontierUbi Avenue 3Singapore408867Tel: +65-6749-8918Fax: +65-6749-8919

SHAWCOR LTD