PENGARUH PRESENTASE ALKALISASI NAOH TERHADAP
KEKUATAN IMPAK MATERIAL KOMPOSIT SERAT DAUN NANAS
POLYESTER DENGAN METODE VACUUM INFUSION
SKRIPSI
Diajukan guna melengkapi tugas akhir dan memenuhi salah satu syarat
untuk menyelesaikan program studi teknik mesin (S1)
dan mencapai gelar sarjana teknik
Oleh :
AHMAD TAUFIQ SHALAHUDDIN
201510120311026
PROGRAM STUDI TEKNIK MESIN
FAKULTAS TEKNIK
UNIVERSITAS MUHAMMADIYAH MALANG
2019
iii
LEMBAR PENGESAHAN
PENGARUH PRESENTASE ALKALISASI NAOH TERHADAP
KEKUATAN IMPAK MATERIAL KOMPOSIT SERAT DAUN NANAS
POLYESTER DENGAN METODE VACUUM INFUSION
Diajukan Kepada
UNIVERSITAS MUHAMMADIYAH MALANG
Untuk Memenuhi Syarat Memperoleh Gelar Sarjana Teknik Program
Strata Satu (S1) Jurusan Teknik Mesin
Disusun Oleh
Ahmad Taufiq Shalahuddin
201510120311026
Diterima dan Disetujui
Pada Tanggal 23 Juli 2019
Dosen Pembimbing I Dosen Pembimbing II
Iis Siti Aisyah, ST., MT., Ph.D Murjito, ST., MT
NIP. 10815030572 NIP. 10894040313
Mengetahui
Ketua Jurusan Teknik Mesin
Murjito, ST., MT
NIP. 10894040313
iv
LEMBAR BIMBINGAN TUGAS AKHIR
Nama : Ahmad Taufiq Shalahuddin
NIM : 201510120311026
No. ST Pembimbing TA : E.2/08/FT/UMM/1/2019
Judul Tugas Akhir : Pengaruh Presentase Alkalisasi NaOH Terhadap
Kekuatan Impak Material Komposit Serat Daun Nanas
Polyester Dengan Metode Vacuum Infusion
Pembimbing I : Iis Siti Aisyah, ST., MT., Ph.D
NO Tanggal URAIAN ASISTENSI TTD
1 19 - 02 - 2019 Judul Segera di Fix kan 1.
2 22 - 02 - 2019 Konsultasi BAB I 2.
3 01 - 03 - 2019 Ok BAB I, Lanjut BAB II 3.
4 07 - 03 - 2019 2.1 Penelitian Terdahulu, 5
Jurnal 4.
5 15 - 03 - 2019 ACC BAB II 5.
6 29 - 03 - 2019 BAB III Pisahkan Bab Bahan
dan Alat 6.
7 04 - 04 - 2019 BAB III Flow Chart Lebih
Detail, Lanjut BAB IV 7.
8 11 - 06 - 2019 BAB IV Pembahasan Sertai
Jurnal 8.
9 15 - 06 - 2019 BAB IV Diagram Blok Diganti
Dengan Garis 9.
10 18 - 06- 2019 BAB V Kesimpulan Sesuaikan
dengan Rumusan Masalah 10.
11 19 - 06- 2019 ACC BAB V, Siapkan Semhas 11.
12 24 - 06- 2019 Konsultasi Naskah Publikasi
Seminar Hasil 12.
13 28 - 06- 2019 ACC Naskah Publikasi
Seminar Hasil 13
Mengetahui, Malang, 23 Juli 2019
Ketua Jurusan Teknik Mesin Dosen Pembimbing I
Murjito, ST., MT Iis Siti Aisyah, ST., MT., Ph.D
NIP. 10894040313 NIP. 10815030572
v
LEMBAR BIMBINGAN TUGAS AKHIR
Nama : Ahmad Taufiq Shalahuddin
NIM : 201510120311026
No. ST Pembimbing TA : E.2/08/FT/UMM/1/2019
Judul Tugas Akhir : Pengaruh Presentase Alkalisasi NaOH Terhadap
Kekuatan Impak Material Komposit Serat Daun Nanas
Polyester Dengan Metode Vacuum Infusion
Pembimbing II : Murjito, ST., MT
NO Tanggal URAIAN ASISTENSI TTD
1 20 - 02 - 2019 Konsultasi Judul 1.
2 23 - 02 - 2019 Konsultasi BAB I 2.
3 02 - 03 - 2019 ACC BAB I 3.
4 07 - 03 - 2019 Konsultasi BAB II 4.
5 16 - 03 - 2019 ACC BAB II 5.
6 29 - 03 - 2019 Konsultasi BAB III 6.
7 05 - 04 - 2019 ACC BAB III 7.
8 12 - 06 - 2019 Konsultasi BAB IV 8.
9 17 - 06 - 2019 ACC BAB IV 9.
10 18 - 06- 2019 Konsultasi BAB V 10.
11 20 - 06- 2019 ACC BAB V 11.
12 24 - 06- 2019 Konsultasi Naskah Publikasi
Seminar Hasil 12.
13 29 - 06- 2019 ACC Naskah Publikasi
Seminar Hasil 13
Mengetahui, Malang, 23 Juli 2019
Ketua Jurusan Teknik Mesin Dosen Pembimbing II
Murjito, ST., MT Murjito, ST., MT
NIP. 10894040313 NIP. 10894040313
vi
SURAT PERNYATAAN
KEASLIAN TULISAN
Yang bertanda tangan di bawah ini
Nama : Ahmad Taufiq Shalahuddin
NIM : 201510120311026
Jurusan : Teknik Mesin
Fakultas : Teknik
: Universitas Muhammadiyah Malang
Dengan ini menyatakan dengan sebenar-benarnya bahwa:
1. Tugas Akhir dengan judul:
“Pengaruh Presentase Alkalisasi Naoh Terhadap Kekuatan Impak Material
Komposit Serat Daun Nanas Polyester Dengan Metode Vacuum Infusion”
Adalah hasil karya saya, dan dalam naskah tugas akhir ini tidak terdapat karya
ilmiah yang pernah diajukan oleh orang lain untuk memperoleh gelar
akademik di suatu Perguruan Tinggi, dan tidak terdapat karya atau pendapat
yang pernah ditulis atau diterbitkan oleh orang lain, baik sebagian ataupun
keseluruhan, kecuali yang secara tertulis dikutip dalam naskah ini dan
disebutkan dalam sumber kutipan dan daftar pustaka.
2. Apabila ternyata di dalam naskah tugas akhir ini dapat dibuktikan terdapat
unsur-unsur PLAGIASI, saya bersedia TUGAS AKHIR ini DIGUGURKAN
dan GELAR AKADEMIK YANG TELAH SAYA PEROLEH
DIBATALKAN, serta diproses sesuai dengan ketentuan hukum yang
berlaku.
3. Tugas akhir ini dapat dijadikan sumber pustaka yang merupakan HAK
BEBAS ROYALTI NON EKSKLUSIF.
Demikian pernyataan ini saya buat dengan sebenarnya untuk dipergunakan
sebagaimana mestinya.
Koordinator
Plagiasi
Koordinator
Naskah Publikasi
Malang, 23 Juli 2019
Yang Menyatakan
M. Irkham Mamungkas, ST.,
MT
Ary Dwiastuti, S. Pd Ahmad Taufiq S.
vii
Abstrak
Penelitian ini bertujuan untuk mengetahui pengaruh presentase alkalisasi
NaOH pada serat daun nanas dan untuk mengetahui kekuatan impak dari komposit
daun nanas. Perlakuan alkalisasi pada serat dengan menggunakan larutan Natrium
Hydroxide (NaOH) secara langsung mempengaruhi struktur serat seperti mengubah
komposisi kimia serat dan meningkatkan kinerja serat alami sebagai penguat
komposit. Konsentrasi larutan NaOH adalah 0%; 3%; 6%; dan 9%. Pada percobaan
ini Serat daun nanas direndam selama 2 jam dalam larutan NaOH. Pembuatan
material komposit mengacu pada ASTM D5942-96 memiliki panjang 62 mm, lebar
10 mm, dan tinggi 10 mm. Kekuatan impak komposit serat daun nanas meningkat
dengan meningkatkan konsentrasi larutan NaOH dan kekuatan impak akan
berkurang setelah melebihi konsentrasi larutan NaOH. Dengan sebanyak 3
spesimen setiap masing-masing variasi larutan NaOH, hasil rata-rata pengujian
impak yang telah dilakukan menunjukkan nilai rata-rata kekuatan impak yang
tertinggi adalah 0,11891 Joule/mm2 dengan konsentrasi larutan NaOH 6%.
Sedangkan dibawahnya dengan konsentrasi larutan NaOH 9% memiliki rata-rata
kekuatan impak 0,110295 Joule/mm2 dan yang paling rendah konsentrasi larutan
NaOH 0% dengan kekuatan impak sebesar 0,017023 Joule/mm2. Kegetasan
komposit serat daun nanas dengan merendam dalam larutan NaOH lebih tinggi
daripada tanpa merendam dalam larutan NaOH. Perendaman pada konsentrasi
larutan NaOH tertinggi menyebabkan kegetasan tertinggi.
Kata Kunci : NaOH; komposit; serat daun nanas; kekuatan impak
viii
Abstract
This research is aimed to know the effect of NaOH alkalization percentage
on pineapple leaf fiber and to know the strength of pineapple composite.
Alkalization process on fiber by using Natrium Hydroxide (NaOH) affected to
structure of fiber directly such as changing chemical fiber composition and
improving fiber performance naturally like composite amplifier. The concentration
of NaOH solution was 0%; 3%; 6% and 9 %. In this experiment, pineapple leaf
fiber was soaked for 2 hours in NaOH solution. Composite materials producer refers
to ASTM D5942-96, it has 62 mm for length, 10 mm for width, and 10 mm for
height. The composite impact power of pineapple leaf fiber has improved by the
progress of NaOH solution and impact power will be decreased after exceeding the
concentration of NaOH solution. With 3 kinds of each NaOH solution, the average
of impact test which has been conducted, showed that the highest score was 0,
11891 Joule/mm2 with NaOH 6%. Whereas below concentration of NaOH solution
9%, has impact power average was 0,110295 Joule/mm2 and the lowest NaOH
concentration solution was 0% with impact power was 0,017023 Joule/mm2. The
concentration of pineapple leaf fiber composites by soaking it in NaOH solution
was higher than without soaking in NaOH solution. Soaking on the highest
concentration of NaOH solution causes the highest tingling..
Keywords : NaOH; composites; pineapple leaf fiber; impact power
ix
KATA PENGANTAR
Segala puji dan syukur kehadirat Allah SWT atas berkah, rahamat dan
hidyah-Nya yang senantiasa dilimpahakan kepada penulis, sehingga bisa
menyelasaikan skripsi dengan judul “PENGARUH PRESENTASE ALKALISASI
NAOH TERHADAP KEKUATAN IMPAK MATERIAL KOMPOSIT SERAT
DAUN NANAS POLYESTER DENGAN METODE VACUUM INFUSION"
sebagai syarat untuk menyelesaiakan Program Sarjana (S1) pada Program Sarjana
Fakultas Teknik Jurusan Teknik Mesin Universitas Muhammadyah Malang.
Dalam penyusunan skripsi ini banyak hambatan serta rintangan yang
penulis hadapi namun pada akhirnya dapat melaluinya berkat adanya bimbingan
dan bantuan dari berbgai pihak baik secara moral maupu spiritual. Untuk itu pada
kesempatan ini penulis menyampaikan ucapan terimakasih kepada:
1. Bapak Murjito, S.T., M.T Selaku Kepala Jurusan Teknik Mesin
Universitas Muhammadiyah Malang.
2. Ibu Iis Siti Aisyah, S.T, M.T., Ph.D Selaku Dosen Pembimbing yang telah
bersedia meluangkan waktu untuk memberikan arahan selama penyusunan
skripsi.
3. Bapak Irkham M.Irkham Mamungkas, S.T,M.T Selaku Dosen yang telah
mengajak saya dalam penelitian ini.
4. Dr.Ir. H. Suwarsono, M.T selaku dosen wali yang telah memberikan
dukungan pengarahan selama masa perkuliahan.
5. Seluruh jajaran Dosen dan Staf Jurusan Teknik Mesin Universitas
Muhammadiyah Malang.
6. Seluruh staf laboratorium UMM & UB yang telah memberikan izin
penelitian dan membantu kelancaran penelitian ini.
7. Kedua Orang tua yang telah memberikan doa dan dukungan moral maupun
dana selama proses pembuatan skripsi.
8. Teman-teman Teknik Mesin UMM & UB 2015, Arief, Nopal, Akbar,
Pudya, Vicky yang selalu memberikan dukungan dalam penelitian skripsi
ini.
x
9. Orang-orang terdekat saya Irmalia, Ari, dan Riyan yang telah memberikan
dukungan penuh dalam menyemangati saya untuk mengerjakan skripsi ini
10. Semua pihak yang tidak dapat disebutkan satu persatu yang telah membantu
memberikan dukungan.
Penulis mohon maaf atas segala kesalahan yang pernah dilakukan. Semoga
skripsi ini dapat memberikan manfaat untuk mendorong penelitian-penelitian
selanjutnya.
Malang, 23 Juli 2019
Ahmad Taufiq Shalahuddin
xi
DAFTAR ISI
LEMBAR JUDUL .................................................................................................. i
POSTER ................................................................................................................. ii
LEMBAR PENGESAHAN ................................................................................. iii
LEMBAR BIMBINGAN TUGAS AKHIR I ..................................................... iv
LEMBAR BIMBINGAN TUGAS AKHIR II ..................................................... v
LEMBAR SURAT PERNYATAAN TIDAK PLAGIASI ................................ vi
ABSTRAK .......................................................................................................... vii
ABSTRACT ........................................................................................................ viii
KATA PENGANTAR .......................................................................................... ix
DAFTAR ISI ........................................................................................................ xi
DAFTAR TABEL ............................................................................................. xiii
DAFTAR GAMBAR ......................................................................................... xiv
BAB I PENDAHULUAN ..................................................................................... 1
1.1 Latar Belakang ........................................................................................... 1
1.2 Rumussan Masalah ..................................................................................... 2
1.3 Tujuan Penelitian ........................................................................................ 3
1.4 Manfaat Penelitian ...................................................................................... 3
1.5 Batasan Masalah ......................................................................................... 3
BAB II TINJAUAN PUSTAKA ........................................................................... 4
2.1 Penelitian Terdahulu ................................................................................... 4
2.2 Komposit .................................................................................................... 7
2.3 Bagian Utama Komposit ............................................................................ 9
2.3.1 Reinforcement................................................................................... 10
2.3.2 Matriks .............................................................................................. 11
2.3.3 Katalis ............................................................................................... 14
2.4 Metode Pembuatan Komposit .................................................................. 14
2.5 Ketangguhan Impak ................................................................................. 18
2.6 Perpatahan Impak ..................................................................................... 19
2.6.1 Patah Getas Patah Ulet...................................................................... 20
2.7 Serat Daun Nanas ..................................................................................... 20
xii
2.7.1 Extraksi Serat Daun Nanas ............................................................... 23
BAB III METODE PENELITIAN .................................................................... 27
3.1 Metode Penelitian ..................................................................................... 27
3.2 Tempat Penelitian ..................................................................................... 27
3.3 Komposisi Komposit Polyester Serat Daun Nanas .................................. 28
3.4 Variabel Penelitian ................................................................................... 28
3.4.1 Variabel Bebas .................................................................................. 28
3.4.2 Variabel Terikat ................................................................................ 29
3.4.3 Variabel Terkontrol .......................................................................... 29
3.5 Penyiapan Alat dan Bahan ....................................................................... 29
3.5.1 Penyiapan Alat .................................................................................. 29
3.5.2 Penyiapan Bahan .............................................................................. 35
3.6 Proses Pelaksanaan ................................................................................... 37
3.6.1 Proses Perendaman Alkali ................................................................ 37
3.6.2 Proses Vacuum Infusion ................................................................... 38
3.7 Pengujian Mekanis Komposit .................................................................. 40
3.7.1 Proses Serat Tunggal ........................................................................ 40
3.7.2 Proses Uji Impak............................................................................... 41
3.8 Flow Chart ................................................................................................ 42
3.9 Kerangka Tabel ........................................................................................ 43
BAB IV HASIL DAN PEMBAHASAN ........................................................... 44
4.1 Hasil Proses Pembuatan Komposit ........................................................... 44
4.2 Data Hasil Pengujian Impak ..................................................................... 45
BAB V KESIMPULAN DAN SARAN .............................................................. 54
5.1 Kesimpulan ............................................................................................... 54
5.2 Saran ......................................................................................................... 54
DAFTAR PUSTAKA .......................................................................................... 56
LAMPIRAN
xiii
DAFTAR TABEL
Tabel 1.1. Physical Characteristics Serat Daun Nanas ......................................... 22
Tabel 1.2 Komposisi Kimia Serat Nanas .............................................................. 25
Tabel 1.3 Komposisi Kimia Serat Nanas pada Metode Proses Pemisahan Serat
yang Berbeda ......................................................................................................... 26
Tabel 3.1 Komposisi Serat Daun Nanas ............................................................... 35
Tabel 3.2 Kekuatan Tarik Serat Tunggal .............................................................. 36
Tabel 3.3 Kerangka Tabel Hasil Pengujian Impak Komposit............................... 43
Tabel 3.4 Kerangka Tabel Hasil Perhitungan Nilai Rata-rata Sudut Setelah
Pengujian ............................................................................................................... 43
Tabel 4.1 Hasil Pengujian Impak Komposit ......................................................... 45
Tabel 4.2 Hasil Perhitungan Nilai Rata-rata Sudut Setelah Pengujian ................. 46
Tabel 4.3 Bentuk Patahan ..................................................................................... 49
xiv
DAFTAR GAMBAR
Gambar 2.1 Komposit partikel ................................................................................ 7
Gambar 2.2 Komposit partikel serpih (flake) .......................................................... 8
Gambar 2.3 Komposit skeltel (filled) ...................................................................... 8
Gambar 2.4 Komposit Laminar............................................................................... 9
Gambar 2.5 (Fibrous Composite) ........................................................................... 9
Gambar 2.6 Metode Hand Lay Up ........................................................................ 15
Gambar 2.7 Metode Vacuum Bag ......................................................................... 16
Gambar 2.8 Pressure Bag ..................................................................................... 16
Gambar 2.9 Metode Filament Winding ................................................................. 17
Gambar 2.10 Metode Continuous Piltrusion ........................................................ 18
Gambar 2.11 Ilustrasi skematis pengujian impak ................................................. 19
Gambar 3.1 Spesimen Uji Impak sesuai ASTM D5942-96 ................................. 28
Gambar 3.2 Alat Uji Impak ................................................................................... 30
Gambar 3.3 Alat Uji Tarik Serat Tunggal ............................................................. 31
Gambar 3.4 Cetakan Uji Impak ............................................................................ 31
Gambar 3.5 Timbangan Digital ............................................................................ 32
Gambar 3.6 Sealent Tape ...................................................................................... 32
Gambar 3.7 Mirror Glaze ..................................................................................... 32
Gambar 3.8 Mesh .................................................................................................. 33
Gambar 3.9 Plastic Bag ........................................................................................ 33
Gambar 3.10 Vacuum compressor ........................................................................ 34
Gambar 3.11 Resin trap ........................................................................................ 34
Gambar 3.12 Kaca ................................................................................................. 34
Gambar 3.13 Alat Bantu Lain ............................................................................... 35
Gambar 3.14 Serat Daun Nanas ............................................................................ 35
Gambar 3.15 Resin dan Katalis ............................................................................. 36
Gambar 3.16 NaOH .............................................................................................. 37
Gambar 3.17 Proses Perendaman NaOH .............................................................. 37
Gambar 3.18 Proses vacuum infusion resin .......................................................... 38
Gambar 3.19 Proses Serat Tunggal ....................................................................... 40
Gambar 3.20 Proses Uji Impak ............................................................................. 41
xv
Gambar 4.1 Spesimen Uji Impak (a) Tanpa Perlakuan Alkali, (b) Perlakuan
Alkali 3%, (c) Perlakuan Alkali 6%, (d) Perlakuan Alkali 9%. ............................ 44
Gambar 4.2 Grafik energi serap variasi presentase NaOH serat daun nanas
terhadap Uji Impak ................................................................................................ 46
Gambar 4.3 Grafik Harga Impak variasi presentase NaOH serat daun nanas
terhadap Uji Impak ................................................................................................ 46
Gambar 4.4 Spesimen Uji Impak setelah diuji (a) Tanpa Perlakuan Alkali,
(b) Perlakuan Alkali 3%, (c) Perlakuan Alkali 6%, (d) Perlakuan Alkali 9%. ..... 48
56
DAFTAR PUSTAKA
Fathoni, Akhmad et al. 2017. “PENGARUH PERLAKUAN PANAS SERAT
TERHADAP SIFAT TARIK SERAT TUNGGAL DAN KOMPOSIT
CANTULA-RHDPE.” Jurnal SIMETRIS 8(1): 67–74.
Hidayat, Pratikno. 2016. “Teknologi Pemanfaatan Serat Daun Nanas Sebagai
Alternatif Bahan Baku Tekstil.” Teknoin 13(2): 31–35.
Matasina, Murizal et al. 2014. “Pengaruh Perendaman Terhadap Sifat Mekanik
Komposit Polyester Berpenguat Serat Buah Lontar.”Jurnal Teknik Mesin
Undana 1(2): 48-58
Refiadi, Gunawan, Koswara, Asep Gunawan. 2005. "Pembuatan Material
Komposit Polimer Dengan Metoda Vacuum Assisted Resin Infusion (VARI)"
Berita Tekhnologi Bahan dan Barang Teknik : 40-45
Utomo, Samuel Budi, Moh Farid, and Haniffudin Nurdiansah. 2017. “Analisis
Proses Pengikisan ( Bleaching ) Dari Hasil Untuk Penguat Bahan Komposit
Absorbsi Suara.” Jurnal Teknik ITS 6(2): 4–8.
Adjiantoro, Bintang et al. 2014 “Pembuatan Material Komposit Matriks.” Majalah
Metalurgi 3: 63-70.
Asroni, Eko Nugroho, 2016. “Pengaruh Komposisi Resin Poliester Terhadap.”
Jurnal Teknik Mesin Univ. Muhammadiyah Metro 5(1): 14–20.
Hadi, Teguh Sulistyo, Sarjito Jokosisworo, and Parlindungan Manik. 2016.
“Analisa Teknis Penggunaan Serat Daun Nanas Sebagai Alternatif Bahan
Komposit Pembuatan Kulit Kapal Ditinjau Dari Kekuatan Tarik, Bending Dan
Impact.” Jurnal Teknik Perkapalan 4(1): 323–31.
Lumintang, Romels C. A., Rudy Soenoko, and Slamet Wahyudi. 2011. “Komposit
Hibrid Polyester Berpenguat Serbuk Batang Dan Serat Sabut Kelapa.” Jurnal
Rekaya Mesin 2(2): 145–53.
Astika, I Made,I Putu Lokantara, and I Made Gatot Karohika. 2013. “Sifat Mekanis
Komposit Polyester dengan Penguat Serat Sabut Kelapa.” Jurnal Energi dan
Manufaktur VI(2): 95-202.
Fajri, Rahmat Iskandar, Tarkono dan Sugiyanto. 2013. “Studi Sifat Mekanik
Komposit Serat Sansevieria Cylindrica Dengan Variasi Fraksi Volume
Bermatrik Polyester.” Jurnal Fema 1(April): 85–93.
Setyanto, R Hari. 2012. “Review : Teknik Manufaktur Komposit Hijau Dan
Aplikasinya.” Performa 11(1): 9–18.
Septiyanto,Rahmat Firman et al 2016. “Serat Sintetis Melalui Uji Tarik Dengan
Bahan Serat Jute Dan E-Glass.” Jurnal Untirta 2(1): 1–11.
Oroh, Jonathan et al. 2013. “Analisis Mekanik Material Komposit Serat Sabut
Kelapa.” Jurnal Universitas Sam Ratulangi Manado : 1-10
Witono, Kris, Yudy Surya Irawan, Rudy Soenoko, and Heru Suryanto. 2013.
57
“Pengaruh Perlakuan Alkali ( NaOH ) Terhadap Morfologi Dan Kekuatan
Tarik Serat Mendong.” Jurnal Rekayasa Mesin 4(3): 227–34.
Irfa'i, Mochamad Arif et al. 2016. “PENGARUH FRAKSI VOLUME SERAT
DAN LAMA WAKTU PERENDAMAN NaOH.” Rotasi 18(1): 1–7.
Wirawan, Willy Artha, Sofyan Arief, Teguh Dwi, and Moch Agus. 2017. “Surface
Modification with Silane Coupling Agent on Tensile Properties of Natural
Fiber Composite.” JEMMME 2(2): 98–105.
Maryanti, Budha, A. As’ad Sonief, and Slamet Wahyudi. 2011. “Pengaruh
Alkalisasi Komposit Serat Kelapa-Poliester Terhadap Kekuatan Tarik.” Jurnal
Rekayasa Mesin 2(2): hal 123-129.
Prasojo, Sugeng, S M Bondan Respati, and Helmy Purwanto. 2014. “( Cocos
Nucifera ) DENGAN MATRIKS POLYESTER.” Jurnal Ilmiah Cendikia
Eksakta : 25–34.