WorkBook RBI ModulePiping 52501
TUJUAN
Dapat melakukan perhitungan laju korosi (corrotion rate), dan sisa umur (remaining life) dari sistem pemipaan drum dan filter.
Dapat menemukan Possibility of Failure (PoF), Consequence of Failure (CoF), Criticality, Confdent Index, serta Inspection Period.
P&I Drawing
Formula (1)A. CORROTION RATE (LAJU KOROSI)
CRI = Ta1 – Ta2
CRII = Ta2 – Ta3
CRIII =
B REMAINING LIFE (SISA UMUR PAKAI)
RL = ta = Ketebalan aktual minimumtr = Ketebalan perhitungan minimumCR= Corrosion Rate
tr = P = Design PressureR = Jari-JariS = Allowable StresE = Longitudinal Weld Efficiency
Formula (2)C Menentukan nilai POF (Probability Of Failure)
1 = Sisa umur masa pakai < 4 tahun2 = Sisa umur masa pakai antara 4-8 tahun3 = Sisa umur masa pakai > 8 tahun
D Menentukan nilai COF (Consequence Of Failure)
1 Faktor STANDBY AVAILABILITY (S)1 = Kegagalan yang menyebabkan Produksi berhenti (plant Shutdown )2 = Kegagalan yang menyebabkan Produksi berkurang (masalah operasi)3 = Kegagalan terjadi namun ada by pass (proses dialihkan ke jalur lain)
2 Faktor FINANSIAL (F)1 = Kerugian Finansial karena kehilangan produksi ≤ 1 hari2 = Kerugian Finansial karena kehilangan produksi antara 1-7 hari3 = Kerugian Finansial karena kehilangan produksi ≥ 1 hari
3 Faktor LOKASI (L)1 = lokasi di area umum dan dapat dievaluasi secaara rutin2 = lokasi terisolasi sehingga butuh ijin khusus3 = Lokasi tertutup ( berada di kepadatan lalu lintas)
RUMUS COF :
COF =
Formula (3)E CRITICALITY
F MAWP (Maximum Allowable Work Pressure)
MAWP =
G INSPECTION FREQUENSI (tahun)
Parameter Confidence Index (CI)0 = Tidak ada keyakinan (Tidak terjadi Kejadian)1 = Deteriorasi yang dapat diprediksi dengan riwayat kejadian terbatas2 = Deteriorasi yang dapat diprediksi dengan riwayat kejadian yang amat bagus3 = Tidak ada mekanisme terjadinay kegagalan yang aktif dan lingkungan operasi yang stabil
Pengolahan Data (1)
DRAWING TECHNICAL DETAILS
TAG No : 52520Diameter : 3 inchWorking Pressure : 145.03 PsiWorking Temperature : 200 FS : 20000
Proces piping Line No 52520 Thickness Data
I II III I II III I II III12 12,20 12,00 11,09 12,20 12,10 12,10 3,20 3,20 3,21
Short Short Long Short Short Long Short Short Long 0,20 0,91 0,56 0,10 0,00 0,05 0,00 -0,01 0,00
3 12,19 12,00 12,00 12,20 12,11 12,11 3,40 3,40 3,40Short Short Long Short Short Long Short Short Long0,19 0,00 0,09 0,09 0,00 0,05 0,00 0,00 0,00
6 12,20 12,00 12,00 12,20 12,20 12,20 3,20 3,20 3,20Short Short Long Short Short Long Short Short Long0,20 0,00 0,10 0,00 0,00 0,00 0,00 0,00 0,00
9 12,11 12,00 12,00 12,20 12,20 12,18 12,20 12,10 12,01Short Short Long Short Short Long Short Short Long0,11 0,00 0,05 0,00 0,02 0,01 0,10 0,09 0,09
B C
PENGOLAHAN DATA PIPING (LINE 52520)
L O K A S IPosisi A
Pengolahan Data (2)
I II III I II III I II III12 12,20 12,00 11,09 12,20 12,10 12,10 3,20 3,20 3,21
Short Short Long Short Short Long Short Short LongCorrosion RateRemaining Life
MAWP
Conclussion
3 12,19 12,00 12,00 12,20 12,11 12,11 3,40 3,40 3,40Short Short Long Short Short Long Short Short Long
Corrosion RateRemaining Life
MAWP
Conclussion
6 12,20 12,00 12,00 12,20 12,20 12,20 3,20 3,20 3,20Short Short Long Short Short Long Short Short Long
Corrosion RateRemaining Life
MAWP
Conclussion
9 12,11 12,00 12,00 12,20 12,20 12,18 12,20 12,10 12,01Short Short Long Short Short Long Short Short Long
Corrosion RateRemaining Life
MAWP
Conclussion
5.403,82546,93
5.480,31
0,1110.865,60
0,11107,69
0,0010.958,605.489,315.448,37 5.448,37
119,42 119,420,20 0,20
OKProses Laminasi, Data refer to nearest, - minimum condition
(A-3)
5.403,82
OK
5.447,47
0,09118,10
5.403,82
Proses Laminasi, Data refer to nearest, - minimum condition
(A-12)
4.989,88
0,1959,83
5.444,32
0,1959,83
OK OK
215,024.989,88
0,9110,71
0,9110,71
Proses Laminasi, Data refer to nearest, - minimum condition
(A-6)
5.447,47
PosisiL O K A S I
A B C
0,02
0,10
OK OK OK
OK OK
Pengolahan Data (3)
RBI CRITICALITY
Consequence of Failure (CoF)
Probability of Failure (PoF)
Rendah Menengah Tinggi
Tinggi 3 2 1
Menengah 4 3 2
Rendah 5 4
Convident Level:
Kode 0 = Tidak ada keyakinan/tidak ada data
Kode 1 = Deteriorasi dapat diprediksi dan data tidak lengkap
Kode 2 = Deteriorasi dapat diprediksi, data cacat diterima standar dan
data lengkap
Kode 3 = Tidak ada mekanisme terjadinya kegagalan yang aktif,
lingkungan operasi yang stabil dan data lengkap
Inspection PeriodCL
0 1 2 3Criticality
1 1 2 6 N/A
2 2 4 6 N/A
3 2 8 8
4 3 8 10 10
5 3 8 10 10
Berdasarkan Confident Level dan tingkat kekritisan, maka didapat periode inspeksi setiap 4 tahun sekali dengan metode inspeksi berdasarkan CoF tinggi dan PoF rendah, adalah:
“UT Method secara parsial setiap 4 tahun sekali”
SpecificationMaterials Science Practical Session Work Book
Dia.(in)
Service Spec. Number Insulation From To SystemPress.(Psi)
Temp.(0C)
Phase S F L
3" GL F03 42243 NO 1-V 4220 52501 211-1 145 (4,35) 150 (93) liquid 1 2 2
2" GL F03 42623 NO 1-V 4260 52501 211-2 145 (4,35) 150 (50) liquid 1 2 2
3" GL F03 52501 NO 42243 & 42623 1-E520E 211-3 145 (4,35) 150 (93) liquid 1 2 2
- - A312 1-E520E YES 52501 52520 211-4 145 (4,35) 150 (50) liquid 1 1 2
3" GL B03 52520 NO 1-E520E 1-V520A 211-5 145 (71,05) 70 (50) liquid 1 2 2
- - A516 1-V520A NO 52520 52120 211-6 145 (71,05) 70 (50) liquid 1 1 2
2" GL B03 52120 NO 1-V520A 1-F520BA 213-1 145 (71,05) 70 (50) liquid 1 2 2
- - A516 1-F520BA NO 52120 522120 213-2 145 (71,05) 70 (50) liquid 3 1 2
2" GL B03 522120 NO 1-F520BA 52401 213-3 145 (71,05) 70 (50) liquid 3 2 2
2" GL B03 52401 NO 522120 1-F520D 213-4 145 (71,05) 70 (50) liquid 1 2 2
- - A516 1-F520D NO 52401 52420 213-5 145 (71,05) 70 (50) liquid 3 1 2
2" GL B03 52420 NO 1-F520D 522220 213-6 145 (71,05) 70 (50) liquid 3 2 2
2" GL B03 522220 NO 52420 1-E520F 213-7 145 (71,05) 70 (50) liquid 1 2 2
- - A312 1-E520F YES 522220 52620 213-8 145 (4,35) 70 (50) liquid 1 1 2
2" GL B03 52620 NO 1-E520F 1-V520H 213-9 145 (4,35) 150 (87) liquid 1 2 2
3" GL B03 52720 YES 1-H520G 1-E520F 215-1 145 (4,35) 150 (132) liquid 1 2 2
- - A312 1-E520F YES 52720 52621 215-2 145 (4,35) 150 (132) liquid 1 1 2
2" GL B03 52621 YES 1-E520F 1-E520E 215-3 145 (4,35) 150 (92) liquid 1 2 2
- - A312 1-E520E YES 52621 52521 215-4 145 (4,35) 150 (93) liquid 1 1 2
3" GL B03 52521 YES 1-E520E 1-V520M 215-5 145 (4,35) 150 (50) liquid 1 2 2
KESIMPULANLaju korosi terbesar di titik A-12 sebesar 0,92mm/tahun.Remaining Life terendah sebesar 10,71 tahun (10 tahun 8
bulan) di titik A-12.Korosi terbesar di titik A-12, dimungkinkan karena adanya
turbulensi akibat pertemuan hot & cold rich glycol dari kedua separator.
MAWP aktual terendah, mengikuti remaining life terendah sebesar 4,989 Psi di titik A-12 dibandingkan dengan desain pressure 72,03 Psi dan MAWP berdasarkan perhitungan awal (standar material spesifikasi) sebesar 558,56 Psi, maka proses piping tersebut aman untuk diinspeksi 4 tahun yang akan datang pada piping line No. 3” GL-F03-52501.