Intro to NDT

مقدهم ای رب تست اهی غیر مخرب

•Penetrant Inspection

•Magnetic Particle Inspection

•Eddy Current Inspection

•Ultrasonic Inspection

•Radiographic Inspection

NDT METHODS

Dye Penetrant Inspection Surface breaking defects only detected

Penetrant applied to the component and drawn into

the defects by capillary action

Applicable to all non- porous and non absorbing

materials.

Penetrants are available in many different types

Water washable contrast

Solvent removable contrast

Water washable fluorescent

Solvent removable fluorescent

Post-emulsifiable fluorescent

Dye Penetrant Inspection

Dye Penetrant Inspection

Step 1. Pre-Cleaning

Cleaning preparation is very important on this method.

Usually solvent removal is been used

Dye Penetrant Inspection

Step 2. Apply penetrant

After the application of the penetrant the penetrant is normally

left on the components surface for approximately 15 minutes

(dwell time). The penetrant enters any defects that may be

present by capillary action

Dye Penetrant Inspection

Step 3. Clean off penetrant

After sufficient penetration time (dwell time) has been

given,excess removal penetrant stage take place. A damped

lint free tissue with solvent is used to clean the excess

penetrant.

Dye Penetrant Inspection

Step 3. Apply developer

After the excess penetrant is been removed, a thin layer

of developer is applied.A penetrant drawn out by reversed

capillary action.

Dye Penetrant Inspection

Step 4. Inspection / development time

Inspection should take place immediately after the developer

has been applied .Any defects present will show as a bleed

out during development time.

Dye Penetrant Inspection

Step 5. Post-Cleaning

After the inspection has been performed post cleaning is

required to prevent corrosion.

Dye Penetrant Inspection

Colour contrast Penetrant

Fluorescent Penetrant Bleed out viewed

under a UV-A light

source

Bleed out viewed

under white light

Magnetic Particle Inspection

Magnetic Particle Inspection

Surface and slight sub-surface detection

Relies on magnetization of component being tested

Ferro-magnetic materials only can be tested

A magnetic field is introduced into a specimen being tested

Methods of applying a magnetic field, yolk, permanent magnet, prods and flexible cables.

Fine particles of iron powder are applied to the test area

Any defect which interrupts the magnetic field, will create a leakage field, which attracts the particles

Any defect will show up as either a dark indication or in the case of fluorescent particles under UV-A light a green/yellow indication

Collection of ink

particles due to

leakage field

Magnetic Particle Inspection

Prods

DC or AC

Electro-magnet

(yolk) DC or AC

Crack like

indication

Crack like

indication

Magnetic Particle Inspection

A crack like

indication

Magnetic Particle Inspection

Alternatively to contrast

inks, fluorescent inks

may be used for greater

sensitivity. These inks

require a UV-A light

source and a darkened

viewing area to inspect

the component

Magnetic Particle Inspection

Typical sequence of operations to inspect a

weld

Clean area to be tested

Apply contrast paint

Apply magnetisism to the component

Apply ferro-magnetic ink to the component

during magnetising

Interpret the test area

Post clean and de-magnatise if required

Magnetic Particle Inspection

Advantages

Simple to use

Inexpensive

Rapid results

Little surface

preparation required

More sensitive than

visual inspection

Disadvantages

Surface or slight sub-

surface detection only

Magnetic materials

only

No indication of

defects depths

Detection is required

in two directions

Basic Principles of Ultrasonic Testing

• To understand and

appreciate the

capability and

limitation of UT

Ultrasonic Inspection Sub-surface detection

This detection method uses high frequency sound

waves, typically above 2MHz to pass through a material

A probe is used which contains a piezo electric crystal

to transmit and receive ultrasonic pulses and display the

signals on a cathode ray tube or digital display

The actual display relates to the time taken for the

ultrasonic pulses to travel the distance to the interface

and back

An interface could be the back of a plate material or a

defect

For ultrasound to enter a material a couplant must be

introduced between the probe and specimen

Ultrasonic Inspection

Ultrasonic testing is a good technique for the

detection of plate laminations and thickness surveys

Laminations detected using compression probes

Ultrasonic Inspection

defect

0 10 20 30 40 50

defect

echo Back wall

echo

CRT Display Compression Probe

Material Thk

initial pulse

Ultrasonic Inspection UT Set, Digital Pulse echo

signals

A scan Display

Compression probe Thickness checking the material

Ultrasonic Inspection

Ultrasonic testing requires high operator for defect

identification

Most weld defects detected using angle probes

Ultrasonic Inspection

Angle Probe

UT Set A Scan

Display

Ultrasonic Inspection

0 10 20 30 40 50

initial pulse defect echo

CRT Display

sound path

Angle Probe

defect

Surface distance

Ultrasonic Inspection Advantages

Rapid results

Sub-surface detection

Safe

Can detect planar defect

Capable of measuring the

depth of defects

May be battery powered

Portable

Disadvantages

Trained and skilled

operator required

Requires high operator

skill

Good surface finish

required

Difficulty on detecting

volumetric defect

Couplant may

contaminate

No permanent record

Radiographic Inspection

The principles of radiography

X or Gamma radiation is imposed upon a test

object

Radiation is transmitted to varying degrees

dependant upon the density of the material through

which it is travelling

Thinner areas and materials of a less density show

as darker areas on the radiograph

Thicker areas and materials of a greater density

show as lighter areas on a radiograph

Applicable to metals,non-metals and composites

Industrial Radiography

• X - Rays

Electrically generated

• Gamma Rays

Generated by the decay

of unstable atoms

Industrial Radiography

• X - Rays

Electrically generated

Industrial Radiography

• Gamma Rays

Generated by the decay of

unstable atoms

Source

Radiation beam Image quality indicator

TWI

Radiographic Inspection

Test specimen Radiographic film

Source

Radiation beam Image quality indicator

Radiographic film with latent image after exposure

Radiographic Inspection

Test specimen

7FE12

Step / Hole type IQI Wire type IQI

Radiographic Sensitivity

Wire Type IQI

Step/Hole Type IQI

Image Quality Indicators

Radiographic Techniques

• Single Wall Single Image (SWSI) - film inside, source outside

• Single Wall Single Image (SWSI) panoramic

- film outside, source inside (internal exposure)

• Double Wall Single Image (DWSI)

- film outside, source outside (external exposure)

• Double Wall Double Image (DWDI)

- film outside, source outside (elliptical exposure)

Single wall single image SWSI

IQI’s should be placed source side

Film

Film

Single wall single image SWSI panoramic

• IQI’s are placed on the film side

• Source inside film outside (single exposure)

Film

Film

Double wall single image DWSI

• IQI’s are placed on the film side

• Source outside film outside (multiple exposure)

• This technique is intended for pipe diameters over 100mm

Double wall single image DWSI

Radiograph

Identification

ID MR11

• Unique identification EN W10

• IQI placing A B • Pitch marks

indicating readable film length

Film

Double wall double image DWDI elliptical exposure

• IQI’s are placed on the source or film side

• Source outside film outside (multiple exposure)

• A minimum of two exposures

• This technique is intended for pipe diameters less than 100mm

Double wall double image DWDI

Shot A Radiograph

Identification

ID MR12

• Unique identification EN W10

• IQI placing

1 2 • Pitch marks indicating readable film length

4 3

TWI

Radiographic Inspection

Advantages

Permanent record

Little surface preparation

Defect identification

No material type

limitation

Disadvantages

Expensive equipment

Bulky equipment ( x-ray )

Harmful radiation

Detection on defect

depending on orientation

Slow results

Required license to operate